Electrical conductivity of K-feldspar at high temperature and high pressure

Author:
Hu, Haiying   Dai, Lidong   Li, Heping   Jiang, Jianjun   Hui, Keshi  


Journal:
Mineralogy and Petrology


Issue Date:
2014


Abstract(summary):

Electrical conductivity measurements on dry polycrystalline K-feldspar were performed at 1.0 to 3.0 GPa and 873 to 1,173 K with a multi-anvil high-pressure apparatus and the Solartron-1260 Impedance/Gain Phase Analyzer in the frequency range of 10(-1) to 10(6) Hz. At each temperature the complex impedance displays a perfect semi-circular arc that represents the grain-interior conduction. Under the experimental conditions, electrical conductivity exponentially increases with increasing temperature and slightly decreases with increasing pressure; however, the effect of pressure on the conductivity is less pronounced than that of temperature. The activation enthalpy decreases slightly from 0.99 to 1.02 eV with increasing pressure, and the activation energy and activation volume for K-feldspar are 0.98 eV and 1.46 +/- 0.17 cm(3)/mol, respectively. According to these Arrhenius parameters, ionic conduction is proposed to be the dominant conduction mechanism in K-feldspar at high temperatures and pressures, and potassium ions are the charge carriers transporting by an interstitial mechanism. The diffusion coefficient of potassium at high temperatures was calculated from our conductivity data on K-feldspar using Nernst-Einstein equation, and the results were compared with the previous experimental results.


Page:
609-618


VIEW PDF

The preview is over

If you wish to continue, please create your membership or download this.

Create Membership

Similar Literature

Submit Feedback

This function is a member function, members do not limit the number of downloads