Annealing behaviour of sub-stoichiometric Ti(C,N)–W mechanical alloy powders

Author:
Kasonde Maweja   L.A. Cornish   Nedret Can  


Journal:
International Journal of Refractory Metals & Hard Materials


Issue Date:
2011


Abstract(summary):

The annealing behaviour of Ti(C 0.5N 0.05)-40wt.% W and Ti(C 0.5N 0.5) 0.6-40 wt.% W mechanically alloyed powders was investigated using XRD, TEM, SEM and DTA techniques. It was observed that the reaction start and finish temperatures between constituents were lower in the system that had higher residual lattice strains after milling. The compositions of the intermetallic compounds and solution phases formed were dependent of the milling conditions and the annealing temperature. Thermal alloying was observed during annealing of Ti(C 0.5N 0.05)-40wt.% W mechanically alloyed products, whereas de-mixing of W-rich phases from the metastable solid solution occurred during annealing of the Ti(C 0.5N 0.5)0.6-40wt.% W milled powders. [All rights reserved Elsevier].


Page:
445-451


VIEW PDF

The preview is over

If you wish to continue, please create your membership or download this.

Create Membership

Similar Literature

Submit Feedback

This function is a member function, members do not limit the number of downloads