home > search >

Annealing effects on microstructure and mechanical properties of chromium oxide coatings RID A-7974-2009

Author:
Pang, Xiaolu  Gao, Kewei  Luo, Fei  Yang, Huisheng  Qiao, Lijie  Wang, Yanbin  Volinsky, Alex A.  


Journal:
THIN SOLID FILMS


Issue Date:
2008


Abstract(summary):

Reactive radio frequency magnetron sputter-deposited chromium oxide coatings were annealed at different temperatures and times. The influence of annealing temperature on the microstructure, surface morphology and mechanical properties was examined by X-ray diffraction, nanoindentation, pin-on-disc wear and scratch tests, respectively. X-ray results show that the chromium oxide sputtered at room temperature in low oxygen flux is primarily amorphous. Annealing below 400 degrees C did not cause much change, while annealing at higher temperature of 500 degrees C caused a significant change in microstructure and mechanical properties. Hardness increased from 12.3 GPa to 26 GPa, and the wearability improved with higher annealing temperature due to the formation of crystalline Cr2O3 phase, which occurs at 470 degrees C. Annealing time had little effect on mechanical properties and microstructure, although coating surface roughness increased with a longer annealing time. Coating adhesion was improved by annealing, due to residual stress relief and possible interfacial interdiffusion. (C) 2007 Elsevier B.V. All rights reserved.


Page:
4685---4689


VIEW PDF

The preview is over

If you wish to continue, please create your membership or download this.

Create Membership

Similar Literature

Submit Feedback

This function is a member function, members do not limit the number of downloads