Precipitation kinetics of 2519A aluminum alloy based on aging curves and DSC analysis

Author:
Yi-ping WU  Ling-ying YE  Yu-zhen JIA  Ling LIU  Xin-ming ZHANG  


Journal:
Transactions of Nonferrous Metals Society of China


Issue Date:
2014


Abstract(summary):

Abstract The precipitation kinetics of 2519A aluminum alloy after different cold rolling reductions before aging was investigated by hardness test and differential scanning calorimetry (DSC). The activation energy was calculated according to DSC curves using single heating rate method. The microstructures of as-rolled and peak-aged alloys were observed by transmission electron microscopy (TEM). The result shows that the age hardenability reduces and the activation energy rises with increasing the reduction from 7% to 40%. Nonuniform dislocations are found in as-rolled alloy and inhomogeneous distribution of θ′ phase is revealed in peak-aged alloy when the reduction is 15%. The inhomogeneous distribution of θ′ phase may be related to the age hardenability reducing and activation energy rising.


Page:
3076-3076


VIEW PDF

The preview is over

If you wish to continue, please create your membership or download this.

Create Membership

Similar Literature

Submit Feedback

This function is a member function, members do not limit the number of downloads