Kinetics of Hydrogen Absorption for Ti33V20Cr47 Alloy Powder

Author:
Xiangcheng, Kong   Junlin, Du   Kun, Wang   Zhilin, Li   Zhu, Wu  


Journal:
Rare Metal Materials and Engineering


Issue Date:
2012


Abstract(summary):

Influences of temperature, initial pressure and particle size on the hydriding reaction kinetics of Ti 33V 20Cr 47 alloy powder was analyzed and discussed. It is found that the rate-controlling step of the hydriding processes is hydrogen diffusion with the activation energy of 25.7+or-0.8 kJ/mol. The reaction rate can be accelerated with the increase of temperature. The Ti 33V 20Cr 47 alloy can finish hydrogen absorption faster under the initial pressure 1.5 MPa and 2.5 MPa than under the initial pressure 3.5 MPa because it has two plateaus. The reaction rate can also be accelerated with the increase of particle size. The possible reason could be related to the fact that the large particle size is adverse for the dissipation of reaction heat, thus leading to the rise of the alloy temperature.


Page:
1899-1902


VIEW PDF

The preview is over

If you wish to continue, please create your membership or download this.

Create Membership

Similar Literature

Submit Feedback

This function is a member function, members do not limit the number of downloads